Porous diamond foam with nanometric diamond grains using Bias Enhanced Nucleation on iridium

Résumé

Porous diamond foam exhibiting a three-dimensional structure was synthesized by applying prolonged Bias Enhanced Nucleation on iridium buffer layers. The Raman spectrum of this material recorded at 325 nm looks very close to the signature obtained for detonation nanodiamonds. HRTEM investigations well confirm the presence of diamond crystals with nanometric size between 2 and 6 nm. All these diamond nanocrystals form a three-dimensional structure very different from ultrananocrystalline diamond (UNCD) generally embedded in a graphitic matrix. According to its high specific surface area, such a 3D material may have promising applications for sensors.

Fichier principal
Vignette du fichier
articleNVaissiere_JCA.pdf (2.28 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Licence
Loading...

Dates et versions

hal-01340054 , version 1 (25-03-2020)

Licence

Identifiants

Citer

N. Vaissiere, Samuel Saada, K.H. Lee, M. Mermoux, Mohamed Sennour, et al.. Porous diamond foam with nanometric diamond grains using Bias Enhanced Nucleation on iridium. Diamond and Related Materials, 2016, 68, pp.23-27. ⟨10.1016/j.diamond.2016.04.009⟩. ⟨hal-01340054⟩
443 Consultations
428 Téléchargements

Altmetric

Partager

  • More