Effect of welding defects on plastic behaviour and fatigue lifetime of friction stir welded Al-Cu-Li alloy
Résumé
The effects of joint line remnant (JLR), kissing bond (KB), and clearance between the sheets (Gap) on tensile and fatigue properties of 2198-T851 friction stir welds have been quantitatively evaluated with respect to a reference weld made using one single sheet. The JLR has no significant influence in the investigated conditions. KB and Gap-induced defects do not significantly influence plastic yield but may induce premature crack initiation by ductile tearing and intergranular decohesions respectively. A critical value for KB opening (280 MPa), a threshold value for fatigue crack propagation from the KB (1 MPa√m) and crack growth rates consistent with literature data have been determined.