Article Dans Une Revue Engineering Failure Analysis Année : 2012

Thermal fatigue failure of brass die-casting dies


This research has been conducted to elucidate the mechanisms of brass die casting failure. A die was examined and we have evaluated the causes of crack failure mechanisms after use in brass die casting. The dominating failure mechanism in the investigated die was thermal fatigue cracking. Crack initiation is associated to accumulation of the local plastic strain that occurs during each casting cycle. The crack growth is facilitated by a number of elements: oxidation of the cracks' surfaces, filling of brass and softening of the die material.



Dates et versions

hal-00675703 , version 1 (01-03-2012)



Dhouha Mellouli, Nader Haddar, Alain Köster, Hassine Ferid Ayedi. Thermal fatigue failure of brass die-casting dies. Engineering Failure Analysis, 2012, 20, pp.137-146. ⟨10.1016/j.engfailanal.2011.11.006⟩. ⟨hal-00675703⟩
187 Consultations
0 Téléchargements



Gmail Facebook X LinkedIn More