Behaviour of oxide scales in hot steel strip rolling

Résumé

The behaviour of oxide scales in the finishing Hot Strip Mill is simulated by the hot Plane Strain Compression Test (PSCT). Compared with the ideal case of homogeneous plastic co-deformation of the oxide layer and the underlying metal, different types of defects are described: delamination at the interface or within the oxide layer; interfacial plastic instability due to the jump of the mechanical properties; perpendicular, through-thickness cracks where the axial strain parallel to the interface dominates, followed by micro-extrusion of metal between the fragments; oblique cracks followed by sliding along the lips, where shear dominates. The Finite Element Method (FEM) is used to bring elements of interpretation, as to which conditions determine each mechanism. Conclusions for the behaviour in hot rolling are sketched

Domaines

Fichier principal
Vignette du fichier
esaform2008_grenier.pdf (270.5 Ko) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Licence
Loading...

Dates et versions

hal-00510343 , version 1 (18-08-2010)

Licence

Identifiants

Citer

Claire Grenier, Pierre-Olivier Bouchard, Pierre Montmitonnet, Martine Picard. Behaviour of oxide scales in hot steel strip rolling. 11th ESAFORM Conference on Material Forming, Apr 2008, Lyon, France. pp.Pages 1227-1230, ⟨10.1007/s12289-008-0163-4⟩. ⟨hal-00510343⟩
287 Consultations
1856 Téléchargements

Altmetric

Partager

  • More